Sabic Thermocomp MCR13S is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added featur

Shenzhen Samtion Chemical Co., Ltd

Sabic Thermocomp MCR13S is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added featur

  • 1
  • 2
  • 3

Brand Name : Sabic Thermocomp

Model Number : MCR13S

Certification : Datasheet,MSDS,ROHS,SGS,REACH,FDA,EU,UL,COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ???

UL Recognized, 94HB Flame Class Rating (3) : ???

Contact Now

Sabic Thermocomp MCR13S resin is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added features
include: Heat Stabilized.


Property

MECHANICAL Value Unit Standard
Tensile Stress, yield, 5 mm/min 48 MPa ISO 527
Tensile Strain, break, 5 mm/min 1 % ISO 527
Flexural Stress, yield, 2 mm/min 65 MPa ISO 178
Flexural Modulus, 2 mm/min 6300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*4 +23°C 20 kJ/m² ISO 180/1U
THERMAL Value Unit Standard
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 131 °C ISO 75/Af
PHYSICAL Value Unit Standard
Mold Shrinkage, flow (5) 0.2 - 0.5 % SABIC Method
Density 1.01 g/cm³ ISO 1183
Source GMD, last updated:2010/01/28

Processing

Injection Molding Value Unit
Drying Temperature 80 °C
Drying Time 4 hrs
Melt Temperature 225 - 250 °C
Front - Zone 3 Temperature 240 - 250 °C
Middle - Zone 2 Temperature 215 - 225 °C
Rear - Zone 1 Temperature 195 - 205 °C
Mold Temperature 30 - 50 °C
Back Pressure 0.2 - 0.3 MPa
Screw Speed 30 - 60 rpm
Source GMD, last updated:2010/01/28
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing
conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or
legacy tooling prior to cutting tools for new molded article.


Other related products we recommend:


Quality Sabic Thermocomp MCR13S is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added featur wholesale

Sabic Thermocomp MCR13S is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added featur Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shenzhen Samtion Chemical Co., Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)